| Product Name | Dia mm | Ref No *1Kg | Specification (*Nearest Specification) | Application |
|---|---|---|---|---|
| Afrox Vitemax | 2.0mm 2.5mm 3.15mm 4.0mm 5.0mm 6.3mm 2.0mm 2.5mm 3.15mm 4.0mm |
W075001 W075002 W075003 W075004 W075005 W075007 W072001* W072002* W072003* W072004* |
AWS A5.1 E6013 | Premium grade general purpose mild steel electrode |
| Afrox Speedcraft | 2.5mm 3.15mm 4.0mm 2.5mm 3.15mm 4.0mm | W075122 W075123 W075124 W072122* W072123* W072124* | AWS A5.1 E6013 | Standard grade general purpose mild steel electrode |
| Afrox Afrolux | 2.5mm 3.15mm 4.0mm 5.0mm 6.3mm | W075202 W075203 W075204 W075205 W075207 | AWS A5.1 E7024 | A heavily coated Premium grade iron powder electrode for high deposition welding of HV fillets and but joints. |
| Superweld Extra | 3.15mm 4.0mm 5.0mm | W075213 W075214 W075215 | AWS A5.1 E7024 | A heavily coated standard grade iron powder electrode for high deposition welding of HV fillets and but joints. |
| Afrox 7018-1 | 2.5mm 3.15mm 4.0mm 5.0mm 6.3mm | W075282 W075283 W075284 W075285 W075287 | AWS A5.1 E7018-1 H8 | A premium grade AC/DC all position low hydrogen electrode. |
| Superweld Ductile | 2.5mm 3.15mm 4.0mm | W075252 W075253 W075254 | AWS A5.1 E7018-1 H4 | A standard grade AC/DC all position low hydrogen electrode. |
| Afrox 78MR | 2.5mm 3.15mm 4.0mm 5.0mm 6.3mm |
W075272 W075273 W075274 W075275 W075277 |
AWS A5.1 E7018-1 H4R | An AC/DC all position low hydrogen electrode. The electrode starts with a low moisture content and the moisture regain is slow. |
| Afrox Ferron 1 | 2.5mm 3.15mm 4.0mm 5.0mm 6.3mm | W075312 W075313 W075314 W075 315 W075317 | AWS A5.1 E7018 H8 | An AC/DC all position low hydrogen electrode. |
| NilSil | 3.2mm 4.0mm | W078034 W078036 | AWS A5.1 E6013* | Nilsil deposits a mild steel weld metal with very low silicone. It is designed specifically for the fabrication and repair of hot dip galvanising baths and lead baths. |
| Ultramild | 3.2mm 4.0mm | W078380 W078381 | AWS A5.1 E6018* | Ultramild gives a soft ductile weld metal designed to absorb shrinkage stresses and minimise the build up of residual stress. |