MMA

Afrox 300

3.15
4.0
5.0

W075603
W075604
W075605

DIN 8555 E1-UM-300-P

26-31

Moderate rolling loads, mild abrasion and frictional loading with good impact resistance. Suitable for rebuilding worn steel or alloy steel machine parts which require machining after welding. It can also be used as an underlayer between base material and harder overlayers

Afrox 350

3.15
5.0

W075607
W075609

DIN 8555 E1-UM-350-P

32-40

High impact and rolling loads with good resistance to mild abrasive wear. Can be machined after welding.

Afrox 400

5.0

W075634

DIN 8555 E1-UM-350-P

32-40

Hard enough to resist serious deformation under fairly heavy impact and rolling loads yet has good resistance to mild abrasive wear. Suitable for metal to metal wear and can be machined after welding

Afrox 452

4.0
5.0

W075674
W075675

DIN 8555 E6-UM-55-GS

53-58

Good resistance to abrasion and impact under rolling loads in both wet and dry conditions. Extremely resistant to breakout and spalling. Machinable with carbide tip tools

Afrox 650A

3.15
4.0

W075623
W075624

DIN 8555 E6-UM-55-GS

53-58

Tool steel type deposit which is resistant to abrasion with moderate impact. Used for metal to metal wear grindable only.

Afrox NiNm

4.0
5.0

W075664
W075665

DIN 8555 E8-UM-200-KP

24 as welded 45-55 work hardened

Non-magnetic austenitic 11-14% manganese deposit for high impact applications. Deposit workhardenes readily under impact. Can also be used to join or hardface C-Mn steel components subject to high impact. The use of an austenitic stainless steel buffer layer is recommended in these cases.

Afrox CrNm

4.0
5.0

W075628
W075629

DIN 8555 E8-UM-200-KP

24 as welded 48-59 work hardened

Non-magnetic austenitic 11-14% manganese deposit for high impact applications. Deposit workhardenes readily under impact. Can also be used to join or hardface C-Mn steel components subject to high impact. The use of an austenitic stainless steel buffer layer is recommended in these cases.

Afrox 600

3.15
4.0
5.0

W075613
W075614
W075615

DIN 8555 E4-UM-55-G

47-65

Martensitic weld metal which has good resistance to fine mineral abrasion with moderate resistance to impact. Use for sandy conditions.

Afrox CR70

3.15
4.0
5.0

W075643
W075644
W075645

DIN 8555 E10-UM-55-R*

50-60

Tough eutectic of austenite and metal carbides that can withstand impact at medium loads under abrasive conditions.

Afrox CR70MR

4.0

W075648

DIN 8555 E10-UM-55-R*

49-59

Tough eutectic of austenite and metal carbides that can withstand impact at medium loads under abrasive conditions.

Afrox Canecrush 60

4.0
5.0

W075654
W077655

DIN 8555 E10-UM-55-R*

56-58

Martensitic matrix with metal carbides for conditions of moderate impact and abrasion.

Afrox Rollgrip 59

4.0

W077657

DIN 8555 E10-UM-50-R*

55

Special electrode depositing large globules of weld metal used for roll roughening in the sugar industry.

Afrox Cobalarc 1

4.0
5.0

W075684
W075685

DIN 8555 E10-UM-55-G*

600HV Matrix 1500 HV Carbides

Chromium carbide deposit which is highly resistant to abrasive wear with moderate impact limited to two layers max. Unmachinable.

Afrox Cobalarc 9

3.15
4.0
5.0

W075593
W075594
W075595

DIN 8555 E10-UM-60-GP*

700-759 HV Matrix 1500 HV Carbides

Complex carbides with primary carbide needles in a matrix of carbide/austenite eutectic. Highly resistant to abrasive wear with high impact loading. Two layers max, unmachinable.

Vantung

4.0
5.0

W077334
W077335

DIN 8555 E21-UM/GF-70-G

2400-2600KHN

Tungsten and Vanadium Carbides in a tough martensitic matrix for extreme abrasive wear.

MHA#1

3.2
4.0
5.0

W077003
W077004
W077005

AWS A5.13 ECoCr-C

46

Cobalt based alloy with excellent properties for metal to metal wear, erosion,corrosion, cold abrasion and hothardness - 40HRc@ 800 deg Celsius. Typical applications, seal rings, cutters, chain saws and dies for dry cell batteries.

2.4
3.2
4.0
5.0

W077012
W077013
W077014
W077015

Cobalt based alloy with excellent properties for metal to metal wear, impact, erosion,corrosion, and hothardness - 30HRc@ 800 deg Celsius. Typical applications; engine valves and extrusion screws. 

3.2
4.0 

3.2