| Product Name | Dia mm | Ref No | Specification (*Nearest Specification) | Hardness HRc | Application |
|---|---|---|---|---|---|
| Tube Alloy 8620-S |
2.4 3.2 |
W077185 W077189 |
DIN8555 UP3-GF-150-P | 12-21 | A low alloy deposit which contains both ferrite and banite. High compressive strength and excellent crack resistance. Ideal for build up prior to hardfacing |
| Tube Alloy BU-S |
3.2 | W077249 | DIN8555 UP1-GF-300-P | 20-30 | A low carbon low alloy deposit used as a build-up on carbon and low alloy steel parts. Machinable. |
| #Tube Alloy 861-S |
2.4 3.2 |
W077235 W077239 |
DIN8555 UP5-GF-45-CGTZ | 21-30 | A premium Cr-Mo Deposit used for build up. It offers superior resistance to softening in service versus mild steel deposits |
| Tube Alloy 242-S |
3.2 3.2 |
W077157 W077159 |
DIN8555 UP1-GF-40-GP | 29-39 | Low alloy deposit with some carbides ideal for metal to metal wear. Machinable |
| Corewear 41-S | 2.4 2.4 3.2 3.2 |
W077294 W077295 W077297 W077299 |
DIN8555 UP1-GF-40-GP | 38-42 | Low alloy deposit with some carbides ideal for metal to metal wear. Machinable |
| Tube Alloy 252-S |
3.2 3.2 |
W077167 W077169 |
DIN8555 UP1-GF-45-GP | 30-45 | Slightly higher alloy content to Tube Alloy 242-S giving higher hardness and suitable for metal to metal wear. |
| Corewear 45-S | 2.4 2.4 3.2 3.2 |
W077284 W077285 W077287 W077289 |
DIN8555 UP1-GF-45-GP | 43-48 | Slightly higher alloy content to Corewear 41-S giving higher hardness and suitable for metal |
| Tube Alloy 258-S |
2.4 2.4 3.2 3.2 |
W077174 W077175 W077177 W077179 |
DIN8555 UP6-GF-50-T | 46-53 | A modifies H-12 tool steel deposit which retains its hardness at high temperatures. Suitable for metal to metal sliding wear. |
| Tube Alloy 410-S |
3.2 3.2 |
W077207 W077209 |
DIN8555 UP3-GF-350-P | 34-42 | An AISI 410 martensitic stainless steel deposit which is crack resistant, corrosion resistant and suitable for metal to metal wear. |
| Tube Alloy 250-S |
3.2 3.2 |
W077217 W077219 |
DIN8555 UP6-GF-50-C | 44-48 | An AISI 420 martensitic stainless steel deposit which is crack resistant, corrosion resistant and suitable for metal to metal wear. |
| Tube Alloy 887-S |
2.4 2.4 3.2 3.2 |
W077264 W077265 W077267 W077269 |
DIN8555 UP5-GF-400-C | 32-40 | An AISI type 414 martensitic stainless steel deposit which is highly resistant to thermal fatigue and fire cracking. |
| Tube Alloy 887N-S |
2.4 2.4 3.2 3.2 |
W077274 W077275 W077277 W077279 |
DIN8555 UP5-GF-45-C | 38-48 | A modified AISI type 414 martensitic stainless steel deposit which is highly resistant to thermal fatigue and fire cracking.The addition of nitrogen improves the resistance to inter bead cracking. |
| Tube Alloy 865-Smod |
2.4 2.4 3.2 3.2 |
W077194 W077195 W077197 W077199 |
DIN8555 UP-GF-45-C | 45-48 | A modified AISI type 410 martensitic stainless steel which is suitable for metal to metal abrasion and has good corrosion resistance. |